| Characteristics |
Klüberpaste HEL 46-450 |
| Article number |
089032 |
| Colour space |
black |
| Service temperature, lower limit |
-40 °C |
| Service temperature, upper limit |
1000 °C |
| Density, Klüber method: PN 024, 20°C |
approx.1.43 g/cm³ |
| Worked penetration, DIN ISO 2137 / ASTM D217, 25°C, lower limit |
325 0.1 mm |
| Worked penetration, DIN ISO 2137 / ASTM D217, 25°C, upper limit |
340 0.1 mm |
| SKF-EMCOR, DIN 51802, Klüber method: distilled water, 168 h |
≤ 1 corrosion degree |
| Flow pressure, DIN 51805-2, -35°C |
≤ 600 mbar |
| Dropping point, DIN ISO 2176 / IP 396 |
≥ 250 °C |
| Four-ball tester, welding load, DIN 51350-4 |
≥ 5000 N |
| Friction coefficient screw test, hexagon bolts M10 x 30-8.8, DIN EN ISO 4017, tightening speed n = 5 min⁻¹, number of screws = 20, nut M10-8, plain and degreased, face material 42CrMo4 with roughness Ra 1.6, tightening torque MA = 50 Nm, averaged bearing surface friction coefficient (initial tightening), external test |
0.11 |
| Friction coefficient screw test, hexagon bolts M10 x 30-8.8, DIN EN ISO 4017, tightening speed n = 5 min⁻¹, number of screws = 20, nut M10-8, plain and degreased, face material 42CrMo4 with roughness Ra 1.6, tightening torque MA = 50 Nm, averaged thread friction coefficient (initial tightening), external test |
0.09 |
| Friction coefficient screw test, hexagon bolts M10 x 30-8.8, DIN EN ISO 4017, tightening speed n = 5 min⁻¹, number of screws = 20, nut M10-8, plain and degreased, face material 42CrMo4 with roughness Ra 1.6, tightening torque MA = 50 Nm, standard deviation (S) of averaged bearing surface friction coefficient (initial tightening), external test |
0.015 |
| Friction coefficient screw test, hexagon bolts M10 x 30-8.8, DIN EN ISO 4017, tightening speed n = 5 min⁻¹, number of screws = 20, nut M10-8, plain and degreased, face material 42CrMo4 with roughness Ra 1.6, tightening torque MA = 50 Nm, standard deviation (S) of averaged thread friction coefficient (initial tightening), external test |
0.01 |
| Friction coefficient screw test, hexagon bolts M10 x 50-A2-70, DIN EN ISO 4017, tightening speed n = 5 min⁻¹, number of screws = 20, material of the nut A2, face material 42CrMo4 with roughness Ra 1.6, tightening torque MA = 40 Nm, averaged bearing surface friction coefficient (initial tightening), external test |
0.09 |
| Friction coefficient screw test, hexagon bolts M10 x 50-A2-70, DIN EN ISO 4017, tightening speed n = 5 min⁻¹, number of screws = 20, material of the nut A2, face material 42CrMo4 with roughness Ra 1.6, tightening torque MA = 40 Nm, averaged thread friction coefficient (initial tightening), external test |
0.11 |
| Friction coefficient screw test, hexagon bolts M10 x 50-A2-70, DIN EN ISO 4017, tightening speed n = 5 min⁻¹, number of screws = 20, material of the nut A2, face material 42CrMo4 with roughness Ra 1.6, tightening torque MA = 40 Nm, standard deviation (S) of averaged bearing surface friction coefficient (initial tightening), external test |
0.006 |
| Friction coefficient screw test, hexagon bolts M10 x 50-A2-70, DIN EN ISO 4017, tightening speed n = 5 min⁻¹, number of screws = 20, material of the nut A2, face material 42CrMo4 with roughness Ra 1.6, tightening torque MA = 40 Nm, standard deviation (S) of averaged thread friction coefficient (initial tightening), external test |
0.03 |
| Water resistance, DIN 51807-1, 3 h, 90°C |
≤ 1 - 90 rating |
| Minimum shelf life from the date of manufacture - in a dry, frost-free place and in the unopened original container, approx. |
24 months |